430 Stainless Steel Sheet is a chromium-based ferritic stainless steel flat product combining good atmospheric corrosion resistance, formability, decorative surface capability and economical material cost.
Unlike 304 stainless steel, Type 430 does not rely on significant nickel alloying and is magnetic in normal conditions. It is widely selected for kitchen equipment, appliance panels, architectural trim, decorative components, automotive trim and general indoor fabrication where the higher corrosion resistance of 304 or 316 is not required.
SAKY STEEL supplies 430 / UNS S43000 / EN 1.4016 stainless steel sheet, plate, coil and strip in hot-rolled and cold-rolled conditions with 2B, BA, No.1, No.4, HL, mirror and other surface finishes.
| Item | Specification |
|---|---|
| Grade | AISI 430 / UNS S43000 / EN 1.4016 |
| Reference Standard | ASTM A240 / ASME SA240 / Customer Specification |
| Product Forms | Sheet / Plate / Coil / Strip / Shim / Custom Cut Pieces |
| Thickness | 0.3 mm – 30 mm |
| Width | 1000 / 1219 / 1500 / 1800 / 2000 / 2500 mm and Custom Widths |
| Length | 2000 / 2440 / 3000 / 5800 / 6000 mm and Custom Lengths |
| Production | Hot Rolled / Cold Rolled |
| Surface Finish | 2B / 2D / BA / No.1 / No.3 / No.4 / HL / No.8 / Mirror / Satin |
| Processing | Cut-to-Size / Slitting / Polishing / Brushing / Protective Film |
| Documentation | MTC / Inspection Documentation as Required |
430 belongs to the ferritic stainless steel family. The following grades are included as comparison references to help buyers understand where 430 sits relative to other commonly used ferritic grades and 304 stainless steel.
| Grade | UNS | EN | Structure | Main Positioning |
|---|---|---|---|---|
| 430 | S43000 | 1.4016 | Ferritic | General-purpose ferritic grade for appliances, decorative parts and mild environments |
| 409 | S40910 | 1.4512 | Ferritic | Lower-chromium stabilized grade widely used for automotive and exhaust applications |
| 439 | S43035 | 1.4510 | Ferritic | Ti-stabilized ferritic grade with improved corrosion resistance, formability and weldability compared with 430 |
| 441 | S43932 / S43940 | 1.4509 | Ferritic | Ti/Nb-stabilized grade used where improved weldability and elevated-temperature performance are useful |
| 304 | S30400 | 1.4301 | Austenitic | Higher-alloy Cr-Ni grade with better general corrosion resistance and greater ductility |
These grades are comparison references and should not be treated as direct equivalents. Final material selection depends on corrosion environment, forming, welding, temperature and cost requirements.
The first table shows the existing 430 composition limits used on this product page. The second table provides typical chemistry of related grades for material-positioning reference.
| Grade | C | Mn | Si | P | S | Cr | Ni |
|---|---|---|---|---|---|---|---|
| 430 | ≤0.12% | ≤1.00% | ≤1.00% | ≤0.040% | ≤0.030% | 16.0–18.0% | ≤0.75% |
| Grade | C | Cr | Ni | Mo | Stabilizing Elements |
|---|---|---|---|---|---|
| 430 | ~0.05% | ~16.2% | — | — | — |
| 409 | ~0.02% | ~11.5% | ~0.2% | — | Ti |
| 439 | ~0.02% | ~17.0% | — | — | Ti |
| 441 | ~0.02% | ~17.5% | — | — | Ti + Nb |
| 304 | ~0.04% | ~18.1% | ~8.1% | — | — |
Typical chemistry values are provided only to illustrate alloy-system differences. Final acceptance should follow the applicable product standard and batch-specific MTC.
Mechanical properties depend on thickness, product form, processing condition and test standard. The existing 430 values are retained below, followed by a broader comparison showing how 430 is positioned against related stainless steel grades.
| Tensile Strength | Yield Strength (0.2% Offset) | Elongation |
|---|---|---|
| 450 MPa | 205 MPa | 22% |
| Grade | Structure | Reference Yield Strength | Reference Elongation | Magnetic | General Position |
|---|---|---|---|---|---|
| 430 | Ferritic | ~280 MPa* | ~20%* | Yes | Balanced cost, appearance and mild-environment corrosion resistance |
| 409 | Ferritic | ~220 MPa* | ~25%* | Yes | Lower-alloy grade commonly associated with exhaust service |
| 439 | Ferritic | ~240 MPa* | ~23%* | Yes | Improved weldability, formability and corrosion resistance over 430 |
| 441 | Ferritic | ~250 MPa* | ~18%* | Yes | Stabilized ferritic grade for welded and elevated-temperature applications |
| 304 | Austenitic | ~230 MPa* | ~45%* | Generally no in annealed condition | Higher ductility and better general corrosion resistance |
*Reference comparison values are intended to show relative material positioning and vary with product form, thickness and specification. They should not be used as universal acceptance criteria.
430 and 304 stainless steel sheets are both widely used, but their alloy structure, corrosion resistance, magnetic behavior and cost are different. Grade selection should be based on the service environment and fabrication requirements.
| Feature | 430 Stainless Steel | 304 Stainless Steel |
|---|---|---|
| Structure | Ferritic | Austenitic |
| Nickel Content | Low / residual nickel | Nickel-alloyed |
| Corrosion Resistance | Suitable for mild atmospheric and indoor environments | Better general corrosion resistance |
| Magnetic | Yes | Generally non-magnetic in annealed condition |
| Relative Material Cost | Generally lower | Generally higher |
| Typical Selection | Appliances, decorative trim, kitchen equipment and indoor architectural parts | Food processing, industrial equipment and more corrosive environments |
430 is not a direct substitute for 304 in every environment. Chloride exposure, cleaning chemicals, temperature, fabrication and required service life should be considered before material selection.
Need help selecting 430, 439, 441 or 304?
Request Material & Size Quote430 stainless steel sheet can be supplied with different surface finishes according to appearance, fabrication and end-use requirements. The original product range includes 2B, BA, No.1, No.3, No.4, HL and polished finishes.
| Finish | Surface Character | Typical Applications |
|---|---|---|
| 2B | Smooth cold-rolled finish with a moderate reflective appearance | Appliances, fabrication, equipment and general sheet applications |
| BA | Bright annealed surface with higher reflectivity | Decorative parts, appliances and visible components |
| No.3 | Coarse polished finish | Kitchen equipment and architectural fabrication |
| No.4 | Brushed / polished finish with a uniform directional appearance | Kitchen equipment, appliances and decorative panels |
| HL | Hairline finish with continuous polishing lines | Interior decoration and architectural components |
| No.1 | Hot-rolled, heat-treated and pickled surface | Industrial fabrication and thicker plate applications |
430 stainless steel sheet can be supplied as standard sheets or processed according to downstream fabrication requirements.
| Processing | Supply Capability |
|---|---|
| Cut-to-Size | Custom width and length according to order requirements |
| Slitting | Sheet and coil can be processed into narrower widths where applicable |
| Polishing | No.3 / No.4 / Hairline and other agreed decorative finishes |
| Protective Film | Available for finished surfaces when required |
| Fabrication | Cutting and other processing requirements can be reviewed according to drawings |
Inspection can be arranged according to the applicable material standard and confirmed purchase requirements. The original 430 sheet page includes both destructive and nondestructive inspection capabilities.
| Inspection Item | Purpose |
|---|---|
| Visual & Dimensional Inspection | Check thickness, width, length, flatness and visible surface condition |
| Chemical Analysis | Verify 430 / UNS S43000 material chemistry |
| Mechanical Testing | Tensile, yield and elongation testing when required |
| Hardness Testing | Verify hardness according to the applicable condition or specification |
| Surface Roughness | Evaluate finished surface where roughness requirements are specified |
| Metallographic Testing | Available when metallurgical examination is required |
| Additional Inspection | Penetrant, corrosion or third-party inspection can be reviewed when applicable and specified before order |
The following report images provide batch-specific inspection evidence for 430 stainless steel sheet. The complete PDF report is available for detailed review of the tested material, inspection items and measured results.
View or download the complete PDF report for detailed inspection records, test results and batch-specific information.
View / Download Full Test Report (PDF)Test results apply to the specific batch or sample shown in the report and should not be interpreted as guaranteed values for all 430 stainless steel sheet supplied.
430 stainless steel sheet is commonly selected for applications requiring an economical ferritic stainless steel with good appearance, formability and corrosion resistance in relatively mild service environments.
| Kitchen Equipment Appliance panels and kitchen components | Home Appliances Refrigerator, dishwasher and equipment panels | Automotive Trim Decorative and interior trim components |
| Architecture Interior panels and decorative fabrication | Food Equipment Selected equipment in mild service conditions | Industrial Fabrication Panels, covers and formed components |
Packaging is selected according to sheet thickness, dimensions, surface finish and transportation requirements. Finished decorative surfaces can receive additional protection to reduce scratching during handling and international shipment.
430 is a ferritic chromium stainless steel commonly identified as UNS S43000 and EN 1.4016. It is widely used for appliances, decorative components and general fabrication in relatively mild corrosion environments.
Yes. 430 is a ferritic stainless steel and is normally magnetic, unlike annealed austenitic grades such as 304.
430 is a ferritic chromium stainless steel with lower alloy cost and magnetic behavior, while 304 is an austenitic chromium-nickel stainless steel with generally better corrosion resistance and broader use in demanding environments.
BA, No.4 and hairline finishes are commonly considered for visible decorative components. The correct finish depends on the required appearance, fabrication process and cleaning conditions.